LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: steel 12C-18CR-9NI-TI (type 316); chromoaluminizinq; sliding friction; wear resistance, сталь 12Х18Н10Т, хромоалітування, тертя ковзання, зносостійкість, УДК 621.785
The structure, phase and chemical composition, microhardness of the surface bands are12Х18N10T after chromoaluminizing chromoaluminizing. It is shown that the wear resistancestali 12Х18N10T in sliding friction without lubrication with protective coatings increases by1.5–5.6 times compared with the original. Розглянуто структуру, фазовий та хімічний склади, мікротвердість поверхневих зон сталі 12Х18Н10Т після хромоалітування. Показано, що зносостійкістьсталі12Х18Н10Т в умовах тертя ковзання без змащування з захисним покриттям зростає в 1,5 – 2,6 разів в порівнянні з вихідною