LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Publisher: National Aviation University
Languages: Ukrainian
Types: Unknown
Subjects:
 Розглянуто вплив температури випробування на механічні характеристики зразків молібденового сплаву ЦМ-10. Показано, що деформований прокаткою молібденовий сплав має анізотропію механічних характеристик. Максимальне значення характеристик міцності досягається на поперечних зразках. Максимальне значення відносного подовження відповідає подовжнім зразкам. Зі збільшенням температури випробування характеристики міцності монотонно знижуються. Пластичні характеристики знижуються в області температур випробування 273–273 К, а надалі різко збільшуються до 25–35 % при температурі випробування 1473 К.  The influence of a test temperature on the mechanical characteristics of the molybdenum alloy samples of CМ-10 is considered. It is shown, that deformed by rolling molybdenum alloy has anisotropy of mechanical characteristics. The maximum value of strength properties is reached on transversal samples. The maximum value of relative elongation corresponds to longitudinal samples. Strength properties of samples are monotonically reduced while test temperature increasing.  Plastic properties in the temperatures range of 273 – 1273 K are reduced, and then they sharply increase reaching 25 – 35 % at test temperature of 1473 К.  Рассмотрено влияние температуры испытания на механические характеристики образцов молибденового сплава ЦМ-10. Показано, что деформированный прокаткой молибденовый сплав обладает анизотропией механических характеристик. Максимальное значение прочностных характеристик достигается на поперечных образцах. Максимальное значение относительного удлинения соответствует продольным образцам. С ростом температуры испытания прочностные характеристики монотонно снижаются. Пластические характеристики снижаются в области температур испытания 273–1273 К, а в дальнейшем резко возрастают до 25–35 % при температуре испытания 1473 К.