LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: composition, iron, self-fluxing alloys, gas-abrasive wear, cutting, destruction, композиція, залізо, самофлюсівний сплав, газоабразивне зношу- вання, різання, руйнування, 620.17 [УДК 621.791]
Studied gas-abrasive wear resistance in the wear of composite materials with iron and selffluxing alloys. Materials with a self-fluxing alloy containing 0, 15, 0 and 50% and 98,5-99,0%density was obtained by compression followed by sintering in the presence of a liquid phase.The methodology of the study and a schematic of the test materials in gas-abrasive wear. Theeffect of the composition, their structure and wear conditions on the resistance. Gas-abrasiveflow attack angle was varied from 15 to 90 degrees. It is shown that the wear tracks flow atangles of gas-abrasive effect on the material smaller than 45°–60° mainly occurs due to theimpact of cutting the abrasive particles. At large angles of 60 ° material wear occurs due tofatigue and brittle fracture. With a decrease in the angle of attack increases the wear resistanceof all compositions. The greatest resistance have the composition with the content of selffluxing alloys for more than 30%. Досліджена зносостійкість при газоабразивному зношуванні композиційнихматеріалів за участю заліза та самофлюсівних сплавів. Вивчено вплив на стійкість складу композицій та умов зношування. Показано, що зношування композицій при кутах дії газоабразивного струменя на матеріал менших за 45-60о восновному відбувається за рахунок різальної дії абразивних частинок. При кутах більших за 60о зношування матеріалу відбувається за рахунок втомногота крихкого руйнування. Найбільшу стійкість мають композиції з вмістомсамофлюсівного сплаву більше ніж 30 %.