LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Publisher: National Aviation University
Languages: Ukrainian
Types: Unknown
Subjects:
 Наведено результати локального наноіндентування поверхні алюмінієвого сплаву Д-16АТ з плакованим шаром і без плакування при різних станах поверхні. Показано, що полірування плакованого матеріалу не створює в ньому істотних внутрішніх напружень.  Results of  local nanoindenting of  the aluminum alloy D-16АТ  surface  with the clad layer and without it are submitted under different surface conditions. It is shown, that the polishing of the clad material does not induce essential internal stresses in one.  Приведены результаты локального наноиндентирования поверхности алюминиевого сплава Д-16АТ с плакированным слоем и без плакировки при разных состояниях поверхности. Показано, что полировка плакированного материала не создает в нем существенных внутренних напряжений.