LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: microhardness; boundary adsorption layers; intensity of wear; lubricant, микротвердость; предельные адсорбционные слои; интенсивность износа; смазочный материал, мікротвердість; граничні адсорбційні шари; інтенсивністьзношування; мастильний матеріал.
There was investigated the intensity of microhardness change of the surface layers of steel 45depending on the surface initial roughness, contact loading and kinetic formation of screeninganti-wear boundary absorption layers on the activated friction surface. It was determined that forcontact surfaces with the initial roughness Rа 0,7 mcm at lubricating of oil commodity compositionТАD-17i and with addition of fullerenes С60 optimal conditions for formation of boundaryabsorption layers create and, independently on contact loading, self-generated organic filmsformat on the whole area of contact zone, which provide increasing of microhardness contactsurfaces and decreasing their wear intensity on 45% at operating time. Исследованы интенсивность изменения микротвердости поверхностных слоев стали 45 в зависимости от начальной шероховатости поверхностей, контактного нагрузки и кинетики формирования на активированной трением поверхности экранирующих противоизносных предельных адсорбционных слоев при смазке элементов трибоспряження трансмиссионним маслом ТАД-17і и ее композицией из нанодисперсных добавкой фуллерен С60.  Досліджено інтенсивність зміни мікротвердості поверхневих шарів сталі 45залежно від початкової шорсткості поверхонь, контактного навантаженнята кінетики формування на активованій тертям поверхні екрануючих протизношувальних граничних адсорбційних шарів при змащуванні елементів трибоспряження трансмісійною оливою ТАД-17і та її композицією з нанодисперсноюдобавкою фулерен С60.