LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Панарін, В. Є.; Інститут металофізики ім. Г.В. Курдюмова НАН України; Фараджаллах, М. А.; Інститут металофізики ім. Г.В. Курдюмова НАН України; Корбут, Є. В.; Національний технічний університет «КПІ» (2013)
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: монокарбід кремнію; тверді сплави; детонаційні покрит- тя; механо-хімічне зношування трибоокиснення, 681.891 [УДК]
В роботі досліджено інтенсивність зношування та коефіцієнти тертя детонаційно-газових покриттів з карбіду кремнію, легованого оксидами хрому та алюмінію, в широкому діапазоні параметрів тертя та температур. Показано, що за таких умов переважає механо-хімічне зношування завдяки утворенню оптимальних оксидних плівок, тому до досліджених покриттів можна підбирати пари тертя з різних матеріалів з мінімальним сумарним зносом. Отримані покриття з карбіду кремнію можна розглядати як альтернативні для заміни покриттів з карбіду вольфраму.