LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Ляшенко, Б.А.; Інститут проблем міцності ім. Г.С. Писаренка НАН України; Мірненко, В.І.; Національна академія оборони України; Солових, Є.К.; Кіровоградський державний технічний університет; Радько, О.В.; Національна академія оборони України (2012)
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: 629.7.083.003.13 (045) [УДК 623.746]
Досліджено хімічний склад та триботехнічні характеристики сталі30ХГСА, зміцненої імпульсним газотермоциклічним іонним азотуван-ням. Виявлено наявність оптимального з огляду на мінімальні інтен-сивність зношування та коефіцієнт тертя діапазону поверхневої кон-центрації азоту, який становить 6,3−7,8 % (залежно від умов роботитрибоз’єднання). Установлено зменшення коефіцієнта тертя й інте-нсивності зношування у 1,5−1,9 та 1,7−2,1 разу відповідно.