LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Кузнецов, Валерій Дмитрович; Пащенко, Валерій Миколайович; Смирнов, Ігор Володимирович; Степанов, Денис Володимирович (2015)
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: dry friction ; abrasion ; wear ; weld surfacing layers ; sprayed coatings, тертя без мащення ; абразивне зношування ; зносостійкість ; на плавлені шари ; напилені покриття
It is shown that the choice of materials to restore the surfaces by weld surfacing for differenttypes of wear is complicated because of general character of existing recommendations. Accordingto the results of experimental studies and tests for conditions of dry friction of metal onmetal recommended compositions with martensitic and metastable austenite structures have nodirect correlation between the hardness and wear resistance. More hard martensitic compositionsno have the higher wear resistance than the less hard composition of the austenitic type.The lack of correlation between the hardness and wear resistance is also observed in the compositionsof high chrome cast iron and structureless martensite which are recommended for abrasivewear conditions. It was found that for the conditions of dry friction it is expedient to usethe compositions and structures of metastable austenite and for the conditions of abrasive wear high chrome cast iron. It is shown that wear resistance for the conditions of dry friction sprayedcoatings on nickel-base much higher than the studied compositions of deposited layers. Показано, що вибір матеріалів при відновленні поверхонь наплавленням для різних видів зношування ускладнюється загальним характером існуючих рекомендацій. Рекомендовані композиції з різним складом і структурою не мають прямої кореляції між твердістю і зносостійкістю. Встановлено, що для умов тертя без мащення доцільно використання наплавлених композицій зі структурами метастабільного аустеніту і напилених покриттів на нікелевій основі, а дляумов абразивного зношування – високохромистого чавуну.