LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
С.Ф. Філоненко; О.П. Космач (2012)
Publisher: National Aviation University
Journal: Vìsnik Nacìonalʹnogo Avìacìjnogo Unìversitetu
Languages: English
Types: Unknown
Subjects: stress, fibres, energy, акустическая эмиссия; амплитуда; закономерность; напряжение; параметр; поперечная сила; энергия, composite material, regularity, акустична емісія; амплітуда; елемент; енергія; залежність; напруження; параметр; поперечна сила, acoustic emission; amplitude; composite material; fibres, energy; parameter; regularity; shear force; stress, amplitude, TL1-4050, parameter, shear force, acoustic emission, 621.316 [621.891], Motor vehicles. Aeronautics. Astronautics
 The simulation of the fracture process of elements of the composite material under the action of shear force and the formation of acoustic emission signals, taking into account changes in the geometric size of the elements of the composite material was conducted. The results of theoretical studies shows that changes in the geometric size of CM elements  affects on the development process of its destruction, and formed AE signal. An increase in the geometric size of CM elements at constant loading conditions, led to decrease in the speed of its destruction. Thus there is a decrease in the amplitude of AE signals, increasing the duration of their leading edge and duration. Was established that an increase in the geometric size of elements of the CM led to reduction of the maximum amplitude, power, energy, and area under the curve of formed AE signals by the linear laws. Such change in the maximum amplitude and duration of formed AE signals, obviously due to the fact that an increase in the geometric size of CM elements decreases the speed of their destruction. Reducing energy and power formed AE signals, probably due to a decrease in the maximum amplitude of formed AE signals by increasing the geometric size of CM elements, which is preceded by an increase in their duration.  Проведено моделирование процесса разрушения элементов композиционного материала при действии поперечной силы и формирование сигналов акустической эмиссии с учетом изменения геометрических размеров элементов композиционного материала. Показано, что изменение геометрических размеров элементов композиционного материала влияет на развитие процесса его разрушения и формируемый при этом сигнал акустической эмиссии. При увеличении геометрических размеров элементов композиционного материала при постоянных условиях нагружения наблюдается уменьшение скорости его разрушения и амплитуды формируемых сигналов акустической эмиссии, увеличение длительности их переднего фронта и длительности.  Проведено моделювання сигналів акустичної емісії при зміні геометричних розмірів елементів композиційного матеріалу, який руйнується поперечною силою. Визначено закономірності зміни амплітудних і енергетичних параметрів формованих сигналів акустичної емісії залежно від геометричних розмірів елементів композиційного матеріалу. Описано отримані залежності з їх статистичними оцінками.