LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Каран, Є. В. (2016)
Publisher: National Aviation University
Languages: Ukrainian
Types: Unknown
Subjects: многоочаговое повреждение; концентраторы напряжения; усталостные тещины; образование и рост трещин; коэффициент интенсивности напряжения; экспериментальный образец, УДК 620.178.2(045), multi-site damage; stress concentrators; fatigue cracks, crack growth and propagation; stress intensity factor, experimental specimen, UDC 620.178.2(045), множинне втомне пошкодження; концентратори напруження; втомні тріщини; поява та ріст тріщин; коефіцієнт інтенсивності напруження; експериментальний зразок
Авиационные конструкции подвергаются циклическим нагрузкам, в следствии чего, у концентраторов напряжения (отверстиях под заклепку) возникают и развиваются усталостные трещины. Развитие усталостных трещин способствует снижению остаточной прочности конструкции и в дальнейшем, ее разрушению. В данной работе рассмотрены вопросы выбора образца для оценки многоочагового повреждения. Методика сверления отверстий под заклепку. Крепление образца на испытательной машине. Обработка результатов эксперимента. Получены данные для роста трещины в авиационном сплаве Д16АТ. Определены коэффициенты С и n уравнения Пэриса, которые характеризируют свойства материала. Построена зависимость скорости роста трещины от коэффициента интенсивности напряжения (КИН). Определена скорость роста трещин и число циклов до появления трещины заданной длины. По экспериментальным данным получен прогноз развития усталостных трещин. Aviation construction subjected to cyclic load, in consequence of which, near stress concentrators (rivet holes), emerge and develop fatigue cracks. The development of fatigue crack reduces the residual strength of the structure and further, its destruction. This work describes the selection of the sample to assess multi-site damage. Technique drilling rivet holes. Mounting the sample on the test machine. Processing of the results of the experiment. The data for crack growth in the aviation alloy D16AT. The coefficients C and n equations Paris Law that characterize properties of the material. The dependence of the crack growth rate of the stress intensity factor (SIF). The rate of crack growth and the number of cycles until a crack of specified length. According to experimental data obtained prediction of fatigue cracks.   о� ����� �Ĺ �о экспериментальным данным получен прогноз развития усталостных трещин.   Авіаційні конструкції піддаються циклічним навантаженням, унаслідок біля концентраторів напруження (отворах під заклепку) виникають і розвиваються втомні тріщини. Розвиток втомних тріщин сприяє зниженню залишкової міцності конструкції і в подальшому її руйнуванню. У даній роботі розглянуто питання вибору зразка для оцінювання множинного втомного пошкодження, методику свердління отворів під заклепку, кріплення зразка на випробувальній машині, а також обробка результатів, отриманих з експерименту. Отримано дані для збільшення тріщин в авіаційному сплаві Д16АТ. Визначено коефіцієнти С і n рівняння Періса, які характеризують властивості матеріалу. Побудовано залежність швидкості збільшення тріщини від коефіцієнта інтенсивності напруження (КІН). Визначено швидкість збільшення тріщин і кількість циклів до появи тріщини заданої довжини. За експериментальними даними отримано прогноз збільшення втомних тріщин.