LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Хижняк, В. Г.; Національний технічний університет «КПІ»; Лоскутова, Т. В.; Національний технічний університет «КПІ»; Аршук, М. В.; Національний технічний університет «КПІ»; Волошановський, П. М.; Національний технічний університет «КПІ» (2013)
Publisher: Національний Авиаційний Університет
Languages: Ukrainian
Types: Unknown
Subjects: УДК 621.891
Наведено результати досліджень упливу захисних покрит-тів за участю титану, алюмінію, ванадію на фазовий склад,структуру та абразивну зносостійкість сталі У8А, Абрази-вну зносостійкість визначали двома методами: закріпленимта вільним абразивами за які використовували карбід бору.Показано вплив мікротвердості, показників тріщиностійко-сті, які визначали методом кінетичної мікротвердості, наабразивну зносостійкість. Установлено, що досліджені вроботі покриття підвищують абразивну зносостійкістьсталі У8А в 2,1–4,3 разу