LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Швець, О.В.; Інститут фізичної хімії імені Л.В. Писаржевського НАН України; Заруба, Л.М.; Інститут фізичної хімії імені Л.В. Писаржевського НАН України; Мишастий, А.Ю.; Інститут фізичної хімії імені Л.В. Писаржевського НАН України; Ільїн, В.Г.; Інститут фізичної хімії імені Л.В. Писаржевського НАН України (2005)
Publisher: National Aviation University
Languages: Ukrainian
Types: Unknown
Subjects:
 Методом темплатного синтезу одержано кілька серій мезоструктурних матеріалів на основі оксидів олова та ванадію (темплати – цетилтриметиламоній бромід, цетилпіридиній бромід, додециламін, додецилсульфат натрію та триблоксополімер поліетиленоксид–поліпропіленоксид–поліетиленоксид Pluronic 123). Показано можливість управління типом (гексагональна, зигзагоподібна, ламелярна) і ступенем упорядкування мезоструктури залежно від природи темплату, співвідношення темплат/Sn, рН та типу реакційного середовища, тривалості старіння, проведення гідротермальної обробки. З’ясовано оптимальні умови видалення темплату та одержання мезопористих матеріалів на основі оксиду олова з вузьким розподілом пор (± 4 Å) у діапазоні D = 22–44 Å, SBET=120–550 м2/г і Vпор до 0,23 см3/г. Досліджено вплив умов синтезу, зокрема, рН реакційної суміші, тривалості синтезу, співвідношення основних компонентів, природи темплату, температури гідротермальної обробки на утворення ламелярних, кубічних та розупорядкованих гексагональних мезоструктур з різним ступенем кристалічності. Показано вплив добавок солей магнію, кобальту, цинку та кадмію на утворення мезофаз та власну кристалізацію сполук ванадію. Після прожарювання при температурі 380 °С в струмені аргону одержано мезопористі матеріали з діаметром пор у діапазоні 27–80 Å, Vпор = 0,10–0,30 см3/г, SBET=80–200 м2/г.  Some series of mesostructural materials on a base of tin oxide and phosphate (templates – cetyltrimethylammonium bromide, cetylpyridinium bromide, dodecylamine, sodium dodecylsulfate and polyethylenoxide–polypropylenoxide–polyethylenoxide triblockcopolimer Pluronic 123) were obtained. The possibility of control of mesostructure type (hexagonal, wormlike, lamellar) and ordering degree by change of template nature, template/Sn ratio, pH and kind of reactionary medium, ageing duration, hydrothermal treatment is shown. Optimal conditions of template removal and creation of mesoporous materials on a base of tin oxide with narrow pore distribution (± 4 Å) over the range D = 22–44 Å, SBET=120–550 m2/g and Vpore till 0,23 cm3/g were determined. The influence of synthesis conditions, in particular, pH of reaction medium, duration of synthesis, ratio of main components, the nature of template, temperature of hydrothermal treatment on formation of lamellar, cubic and disordered hexagonal mesostructures with different degree of crystallinity was studied. The influence of magnesium, cobalt, zinc and cadmium on formation of mesophases and own crystallization of vanadium oxide was shown. Calcinations at 380 °C in argon flow gave mesoporous materials with pore diameter between 27–80 Å, Vпор = 0,10–0,30 cm3/g, SBET=80–200 m2/g .  Методом темплатного синтеза получены несколько серий мезоструктурных материалов на основе оксидов олова и ванадия (темплаты – цетилтриметиламмоний бромид, цетилпиридиний бромид, додециламин, додецилсульфат натрия и триблоксополимер полиэтиленоксид–полипропилэноксид–полиэтиленоксид Pluronic 123). Показана возможность управления типом (гексагональная, зигзагообразная, ламеллярная) и степенью упорядочения мезоструктуры в зависимости от природы темплата, соотношения темплат/Sn, рН и типа реакционной среды, длительности старения, проведения гидротермальной обработки. Выяснены оптимальные условия удаления темплата и получения мезопористых материалов на основе оксида олова с узким распределением пор(± 4 Å) в диапазоне D = 22–44 Å, SBET=120–550 м2/г и Vпор до 0,23 см3/г. Исследовано влияние условий синтеза, в частности, рН реакционной среды, длительности синтеза, соотношения основных компонентов, природы темплата, температуры гидротермальной обработки на образование ламеллярных, кубических и разупорядоченных гексагональных мезоструктур с различной степенью кристалличности. Показано влияние  добавок солей магния, кобальта, цинка и кадмия на образование  мезофаз и собственную кристаллизацию соединений ванадия. После прокаливания при температуре 380 °С в струе аргона получены мезопористые материалы с диаметром пор в диапазоне 27–80 Å, Vпор = 0,10–0,30 см3/г, SBET=80–200 м2/г.