LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Illana, Andrea; Mato, Sonia; Ehiasarian, Arutiun; Purandare, Yashodhan; Lasanta, Maria; Miguel, Maria; Hovsepian, Papken; Trujillo, Francisco (2017)
Publisher: Springer
Languages: English
Types: Article
Subjects:
The main objective of this work was to evaluate the oxidation resistance of three PVD-HIPIMS CrN/NbN coatings, studying the effect of the surface finishing of the substrate and the role of niobium content into the coating composition. CrN/NbN nano-multilayered films on P92 steel were tested at 650°C in pure steam atmosphere. The mass gain was measured at fixed intervals to study their oxidation kinetics. The morphology and thickness of nanoscales were measured by transmission electron microscopy (TEM). Characterization of coatings before and after the thermal treatment was performed by scanning electron microscopy-energy with facilities of dispersive X-ray spectroscopy (SEM–EDX) and X-ray diffraction (XRD). All coatings improved the oxidation resistance of the substrate material, but the best behaviour was exhibited by the CrN/NbN with the high niobium (Nb) content and deposited on the substrate with the finest surface finishing.