LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Sheafi, E.M.; Tanner, K.E. (2015)
Publisher: Elsevier
Languages: English
Types: Article
Subjects:

Classified by OpenAIRE into

mesheuropmc: technology, industry, and agriculture
Different cyclic loading modes have been used in in vitro fatigue studies of PMMA bone cement. It is unclear which loading mode is most appropriate from the perspective of the in vivo loading experienced by the cement in a cemented arthroplasty. Also, in different in vitro fatigue studies, different test specimen configurations have been used. The present work considers the influence of test specimen fabrication method (direct moulding versus moulding followed by machining) and cross-section shape (rectangular versus circular) on the tension-tension fatigue performance of two bone cement brands (SmartSet GHV and CMW1), under force control conditions. Two trends were consistent: 1) for each of the cements, for molded specimens, a longer fatigue life was obtained with circular cross-sectioned specimens and, 2) for either rectangular or circular CMW1 specimens, a longer fatigue life was obtained using machined specimens. A comparison of the present results to those reported in our previous work on fully-reversed tension-compression loading under force control showed that, regardless of the test specimen fabrication method or cross-section configuration used, the fatigue life was considerably shorter under tension-compression than tension-tension loading. This finding highlights the fact the presence of the compression portion in the loading cycle accelerates fatigue failure.