LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Tsui, H.C.L.; Goff, L.E.; Barradas, N.P.; Alves, E.; Pereira, S.; Palgrave, R.G.; Davies, R.J.; Beere, H.E.; Farrer, I.; Ritchie, D.A.; Moram, M.A. (2016)
Publisher: IOP Publishing
Languages: English
Types: Article
Subjects:
Four different methods for measuring the compositions of epitaxial ScxGa1-xN films were assessed and compared to determine which was the most reliable and accurate. The compositions of epitaxial ScxGa1-xN films with 0 ≤ x ≤ 0.26 were measured directly using Rutherford backscattering (RBS) and x-ray photoelectron spectroscopy (XPS), and indirectly using c lattice parameter measurements from x-ray diffraction and c/a ratio measurements from electron diffraction patterns. RBS measurements were taken as a standard reference. XPS was found to underestimate the Sc content, whereas c lattice parameter and c/a ratio were not reliable for composition determination due to the unknown degree of strain relaxation in the film. However, the Sc flux used during growth was found to relate linearly with x and could be used to estimate the Sc content.
  • The results below are discovered through our pilot algorithms. Let us know how we are doing!

    • [1] Morkoc H, Strite S, Gao G B, Lin M E, Sverdlov B and Burns M 1994 J. Appl. Phys. 76 1363
    • [2] Khan A, Balakrishnan K and Katona T 2008 Nat. Photonics 2 77
    • [3] Davydov V Yu, Klochikhin A A, Seisyan R P, Emtsev V V, Ivanov S V, Bechstedt F, Furthmuller J, Harima H, Mudryi A V, Aderhold J, Semchinova O and Graul J 2002 phys. stat. sol (b) 229 R1
    • [4] Kneissl M, Kolbe T, Chua C, Kueller V, Lobo N, Stellmach J, Knauer A, Rodriguez H, Einfeldt S, Yang Z, Johnson N M and Weyers M 2011 Semicond. Sci. Technol. 26 014036
    • [5] Moram M A and Zhang S 2014 J. Mater. Chem. A 2 6042
    • [6] Knoll S M, Rovezzi M, Zhang S, Joyce T B, Moram M A 2014 J. Phys. D: Appl. Phys. 26 225801
    • [7] Knoll S M, Zhang S, Joyce T B, Kappers M J, Humphreys C J, Moram M A 2012 phys. stat. sol. (a) 209 33
    • [8] Knoll S M, Rhode S K, Zhang S, Joyce T B, Moram M A 2014 Appl. Phys. Lett. 104 101906
    • [9] Constantin C, Al-Brithen H, Haider M B, Ingram D and Smith A R 2004 Mat. Res. Soc. Symp. Proc. 799 Z9.5
    • [10] Constantin C, Al-Brithen H, Haider M B, Ingram D and Smith A R 2004 Phys. Rev. B 70 193309
    • [11] Constantin C, Haider M B, Ingram D, Smith A R, Sandler N, Sun K and Ordejon P 2005 J. Appl. Phys. 98 123501
    • [12] Deng R, Evans S R and Gall D 2013 Appl. Phys. Lett. 102 112103
    • [13] Deng R, Jiang K and Gall D 2014 J. Appl. Phys. 115 013506
    • [14] Zhang S, Holec D, Fu W Y, Humphreys C J and Moram M A 2013 J. Appl. Phys. 114 133510
    • [15] Zhang S, Fu W Y, Holec D, Humphreys C J and Moram M A 2013 J. Appl. Phys. 114 243516
    • [16] Moram M A, Zhang Y, Joyce T B, Holec D, Chalker P R, Mayrhofer P H, Kappers M J and Humphreys C J 2009 J. Appl. Phys. 106 113533
    • [17] Tsui H C L, Goff L E, Barradas N P, Alves E, Pereira S, Beere H E, Farrer I, Nicoll C A, Ritchie D A and Moram M A 2015 phys. stat. sol. (a) 212 2837
    • [18] Tsui H C L, Goff L E, Rhode S K, Pereira S, Beere H E, Farrer I, Nicoll C A, Ritchie D A and Moram M A 2015 Appl. Phys. Lett. 106 132103
    • [19] Akiyama M, Kamohara T, Kano K, Teshigahara A, Takeuchi Y and Kawahara N 2009 Adv. Mater. 21 593
  • No related research data.
  • No similar publications.

Share - Bookmark

Cite this article