LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Nyangasi, Leah O.; Andala, Dickson M.; Onindo, Charles O.; Ngila, Jane C.; Makhubela, Banothile C. E.; Ngigi, Eric M. (2017)
Publisher: Hindawi
Journal: Journal of Nanomaterials
Languages: English
Types: Article
Subjects: Technology (General), T1-995, Article Subject
TiO2 fibers were prepared through electrospinning of poly methyl methacrylate (PMMA) and titanium isopropoxide (TIP) solution followed by calcination of fibers in air at 500°C. Cetyltrimethylammonium bromide (CTAB) protected palladium nanoparticles (Pd NPs) prepared through reduction method were successfully adsorbed on the TiO2 nanofibers (NF). Combined studies of X-ray diffraction (XRD), scanning electron microscope (SEM), and transmission electron microscope (TEM) indicated that the synthesized Pd/TiO2 had anatase. BET indicated that the synthesized TiO2 and Pd/TiO2 had a surface area of 53.4 and 43.4 m2/g, respectively. The activity and selectivity of 1 mol% Pd/TiO2 in the Heck reaction have been investigated towards the Mizoroki-Heck carbon–carbon cross-coupling of bromobenzene (ArBr) and styrene. Temperature, time, solvent, and base were optimized and catalyst was recycled thrice. 1H NMR and 13C NMR indicated that stilbene, a known compound from literature, was obtained in various Heck reactions at temperatures between 100°C and 140°C but the recyclability was limited due to some palladium leaching and catalyst poisoning which probably arose from some residual carbon from the polymer. The catalyst was found to be highly active under air atmosphere with reaction temperatures up to 140°C. Optimized reaction condition resulted in 89.7% conversions with a TON of 1993.4 and TOF value of 332.2 hr−1.