LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
LIU Jing-ru; XIA Yang-yang; GAO Li-qun; YU Qiang (2017)
Publisher: Journal of Materials Engineering
Journal: Journal of Materials Engineering
Languages: Chinese
Types: Article
Subjects: high impact polystyrene (HIPS), high density polyethylene (HDPE), blend, dynamic viscoelastic behavior, phase morphology, compatibilizer, Materials of engineering and construction. Mechanics of materials, TA401-492
The dynamic viscoelastic behavior and phase morphology of high impact polystyrene (HIPS)/high density polyethylene (HDPE) blends were investigated by dynamic rheological test and scanning electron microscopy (SEM). The compatibilizing effect of 1%(mass fraction, same as below) micron-CaCO3 and nano-CaCO3 on HIPS/HDPE(30/70) immiscible blend was compared. The results indicate that the complex viscosity and storage modulus of HIPS/HDPE blends at low frequencies show positive deviation from the mixing rule when HDPE is less than 30%, while negative deviation is observed when HDPE is more than 30%. The former is related to the interaction between HDPE and PB particles and the latter is attributed to the poor interfacial interaction between HDPE matrix and PS particles. When HIPS is the matrix phase, HDPE particles display broad size distribution. When HDPE acts as a matrix phase, PS dispersed phase exhibits bimodal size distribution corresponding to the presence of two different types of PS dispersed particles. 1% nano-CaCO3 has a certain compatibilizing effect on HIPS/HDPE(30/70) immiscible blend, which is mainly located at HIPS/HDPE interface and in the HDPE matrix, while micron-CaCO3 acts as viscosifier rather than compatibilizer, which is confined in the HDPE matrix.