Kondo, Toshihiro; Takakusagi, Satoru; Uosaki, Kohei (2009)
Publisher: Elsevier B.V.
Journal: Electrochemistry Communications
Languages: English
Types: Article
Subjects: Underpotential deposition (upd), Surface X-ray scattering (SXS), Ag on Au(111)
Stability of underpotentially deposited (upd) Ag layers on Au(111) surface was investigated by surface X-ray scattering (SXS). While the complete pseudomorphic Ag bilayer on Au(111) surface obtained by upd at 10 mV (vs. Ag/Ag+) was maintained its structure even after the circuit was disconnected and the surface was exposed to ambient atmosphere, the pseudomorphic Ag monolayer obtained by upd at 50 mV was converted to a partial bilayer with the coverage of 0.66 ML and 0.46 ML for the 1st and 2nd layer, respectively. These results show that Ag bilayer is structurally more stable than Ag monolayer on Au(111) and Ag atoms of the upd monolayer move around on the Au(111) surface without potential control.
  • No references.
  • No related research data.
  • No similar publications.

Share - Bookmark

Download from

Cite this article

Collected from

Cookies make it easier for us to provide you with our services. With the usage of our services you permit us to use cookies.
More information Ok