LOGIN TO YOUR ACCOUNT

Username
Password
Remember Me
Or use your Academic/Social account:

CREATE AN ACCOUNT

Or use your Academic/Social account:

Congratulations!

You have just completed your registration at OpenAire.

Before you can login to the site, you will need to activate your account. An e-mail will be sent to you with the proper instructions.

Important!

Please note that this site is currently undergoing Beta testing.
Any new content you create is not guaranteed to be present to the final version of the site upon release.

Thank you for your patience,
OpenAire Dev Team.

Close This Message

CREATE AN ACCOUNT

Name:
Username:
Password:
Verify Password:
E-mail:
Verify E-mail:
*All Fields Are Required.
Please Verify You Are Human:
fbtwitterlinkedinvimeoflicker grey 14rssslideshare1
Slaby, Stefan Andreas (2015)
Publisher: KIT, Karlsruhe
Languages: German
Types: Doctoral thesis
Subjects: Mechanische Eigenschaften, Mikromechanisches Prüfen, mechnical properties, small scale testing, µPIM, Engineering & allied operations, Ermüdung, 17-4PH stainless steel, fatigue, Mikrostruktur, 17-4PH Edelstahl, Mikropulverspritzguss
ddc: ddc:620
Im Rahmen der vorliegenden Arbeit wurde ein Mikro-Testverfahren entwickelt, mit dem die Zug- und Ermüdungseigenschaften von mikropulverspritzgegossenen (µPIM) Bauteilen aus 17 4PH Edelstahl gemessen wurden. Der Vergleich mit konventionell hergestelltem Material zeigte, dass das µPIM Material bereits gute mechanische Eigenschaften aufweist, im Bereich der Mikrostruktur aber noch Optimierungsbedarf besteht.